The volume fraction and morphology of the TCP-phase formed in two kinds of Ni-Mo-Cr-Re superalloys under different heat treatment conditions were investigated in this paper. In Re-5% alloy, with increasing of the heat treatment temperature and prolonging the holding time, the volume fraction of TCP-phase decreased and the TCP-phase size increased. At relatively lower temperature, the TCP-phase prefers to present in the dendrite cores. In Re-10% alloy, the volume fraction and size have the same change tendency as that of in Re-5% alloy, but the morphology will change from needle-like and block-like to sphere when the temperature increases. The TCP-phases formed in these two Ni-Mo-Cr-Re alloys are σ and P phase.
关键词:
Heat treatment
,
null
,
null
Pingli MAO
,
Ke YANG
,
Guoyue SU
材料科学技术（英）
The hot deformation behavior of an as-cast 0Cr17Mn14Mo2N duplex stainless steel has been studied by hot compression test at the temperature range from 1000℃ to 1200℃, and the strain rates are 0.1 s-1, 1 s-1 and 5 s-1, respectively. It was found that during hot deformation there is only dynamic recovery taking place within the δ-ferrite phase, but the γ-austenite phase undergoes dynamic recrystallization. The activation energy of the steel for hot compression is estimated to be 480 kJ/mol.
关键词:
Hot deformation
,
null
,
null